TRU-GALV® Silver Pro Galvanizing Compound
PRODUCT DATA
TRU-GALV® Silver Pro Galvanizing Compound STOCK# 065-017-026 PRODUCT DESCRIPTION
Silver Pro Galvanize Paint is a sacrificial coating that inhibits rust and corrosion to ferrous metals. An excellent, fast drying touch-up for repair of galvanized substrates. This primer has the bright finish of a hot-dip galvanized coating. USES • Refineries • Welds • Fences •Gutters • Bridges
• Wrought iron • Power plants • Farm Equipment • Automotive • Marine
• Damaged galvanized surfaces • Highway maintenance • Nuclear facilities • Transmission towers • Structural steel DIRECTIONS FOR USE Preparation Remove all rust, scale, paint, grease or foreign matter. A good clean surface is necessary. Apply directly to DRY metal or galvanized surface and not over any other paint or coating. Product should be sprayed in a wellventilated area. • Use between 50°F (10°C) and 90°F (32°C). For For Best Results: • Turn can upside down. • Hit sides lightly while rotating can 1/4 turns until steel mixing ball breaks loose.
DIRECTIONS CONTINUED
Then hold can at top and swing bottom of can in a circle for 30 45 seconds, or until ball travels freely in bottom groove. Repeat after each minute of use. Do not shake can up and down. PRODUCT DATA Press spray button firmly with the can 8” to 12” from surface being coated. Move can with short dusting strokes, releasing button at the end of each stroke. Apply several thin coats. To prevent clogging, clear the valve by holding can upside down and spray until only clear gas comes out. TECHINICAL DATA Corrosion resistance 5% salt fog @ 100°F. - 200 hrs. minimum Dry heat resistance 400°F. sustained Wet heat resistance (nonimmersion) 100°F. Dries to touch 30 minutes To recoat 2 to 16 hrs. or after 36 hrs. Recommended dry film thickness 1.5 to 3.0 mils Dry film weight - Zinc Dust 69% - Resin 31% Specific gravity (#/gal.)- 6.33 (g./ml)- 0.76 VOC (% by wt.)
TECHNICAL DATA
47.5 HMIS (NFPA) Rating 231 Flashpoint Below 0°F. RESISTANCE GUIDE (Resistance to fumes, splash and spillage; not immersion) •Aliphatic hydrocarbon solvents Light • Alkalis Light • Aromatic hydrocarbon solvents Severe • Chlorinated solvents Severe • Fresh water and salt water Light • Glycol ethers, alcohols, formaldehyde Moderate • Inorganic acids Moderate • Oils (cutting, vegetable, lubricating) Light • Organic acids Moderate • Oxygenated solvents Moderate PERFORMANCE • Weld-through primer • VOC compliant • Dry to touch in 30 minutes • Hot dip appearance
- Meets ASTM A780-01
Revised 8/2017
.
TRU-GALV® Silver Pro Galvanizing Compound STOCK# 065-017-026 PRODUCT DESCRIPTION
Silver Pro Galvanize Paint is a sacrificial coating that inhibits rust and corrosion to ferrous metals. An excellent, fast drying touch-up for repair of galvanized substrates. This primer has the bright finish of a hot-dip galvanized coating. USES • Refineries • Welds • Fences •Gutters • Bridges
• Wrought iron • Power plants • Farm Equipment • Automotive • Marine
• Damaged galvanized surfaces • Highway maintenance • Nuclear facilities • Transmission towers • Structural steel DIRECTIONS FOR USE Preparation Remove all rust, scale, paint, grease or foreign matter. A good clean surface is necessary. Apply directly to DRY metal or galvanized surface and not over any other paint or coating. Product should be sprayed in a wellventilated area. • Use between 50°F (10°C) and 90°F (32°C). For For Best Results: • Turn can upside down. • Hit sides lightly while rotating can 1/4 turns until steel mixing ball breaks loose.
DIRECTIONS CONTINUED
Then hold can at top and swing bottom of can in a circle for 30 45 seconds, or until ball travels freely in bottom groove. Repeat after each minute of use. Do not shake can up and down. PRODUCT DATA Press spray button firmly with the can 8” to 12” from surface being coated. Move can with short dusting strokes, releasing button at the end of each stroke. Apply several thin coats. To prevent clogging, clear the valve by holding can upside down and spray until only clear gas comes out. TECHINICAL DATA Corrosion resistance 5% salt fog @ 100°F. - 200 hrs. minimum Dry heat resistance 400°F. sustained Wet heat resistance (nonimmersion) 100°F. Dries to touch 30 minutes To recoat 2 to 16 hrs. or after 36 hrs. Recommended dry film thickness 1.5 to 3.0 mils Dry film weight - Zinc Dust 69% - Resin 31% Specific gravity (#/gal.)- 6.33 (g./ml)- 0.76 VOC (% by wt.)
TECHNICAL DATA
47.5 HMIS (NFPA) Rating 231 Flashpoint Below 0°F. RESISTANCE GUIDE (Resistance to fumes, splash and spillage; not immersion) •Aliphatic hydrocarbon solvents Light • Alkalis Light • Aromatic hydrocarbon solvents Severe • Chlorinated solvents Severe • Fresh water and salt water Light • Glycol ethers, alcohols, formaldehyde Moderate • Inorganic acids Moderate • Oils (cutting, vegetable, lubricating) Light • Organic acids Moderate • Oxygenated solvents Moderate PERFORMANCE • Weld-through primer • VOC compliant • Dry to touch in 30 minutes • Hot dip appearance
- Meets ASTM A780-01
Revised 8/2017
.